Abstract
Some photosensitive resins have poor mechanical properties after 3D printing. To overcome these limitations, a polyurethane acrylate oligomer (PUA) microsphere was prepared using the Pickering emulsion template method and ultraviolet (UV) curing technology in this paper. The prepared PUA microspheres were added to PUA-1,6-hexanediol diacrylate (HDDA) photosensitive resin system for digital light processing (DLP) 3D printing technology. The preparation process of PUA microspheres was discussed based on micromorphology, and it was found that the oil-water ratio of the Pickering emulsion and the emulsification speed had a certain effect on the microsphere size. As the oil-water ratio and the emulsification speed increased, the microsphere particle size decreased to a certain extent. Adding a suitable proportion of PUA microspheres to the photosensitive resin can improve the mechanical properties and thermal stability. When the modified photosensitive resin microsphere content was 0.5%, the tensile strength, elongation at break, bending strength, and initial thermal decomposition temperature were increased by 79.14%, 47.26%, 26.69%, and 10.65%, respectively, compared with the unmodified photosensitive resin. This study provides a new way to improve the mechanical properties of photosensitive resin 3D printing. The resin materials studied in this work have potential application value in the fields of ceramic 3D printing and dental temporary replacement materials.