Abstract
This study investigated the microstructures, mechanical performances, corrosion resistances, and in vitro studies of porous Ti-xNb-10Zr (x: 10 and 20; at. %) alloys. The alloys were fabricated by powder metallurgy with two categories of porosities, i.e., 21-25% and 50-56%, respectively. The space holder technique was employed to generate the high porosities. Microstructural analysis was performed by using various methods including scanning electron microscopy, energy dispersive spectroscopy, electron backscatter diffraction, and x-ray diffraction. Corrosion resistance was assessed via electrochemical polarisation tests, while mechanical behavior was determined by uniaxial compressive tests. In vitro studies, such as cell viability and proliferation, adhesion potential, and genotoxicity, were examined by performing an MTT assay, fibronectin adsorption, and plasmid-DNA interaction assay. Experimental results showed that the alloys had a dual-phase microstructure composed of finely dispersed acicular hcp α-Ti needles in the bcc β-Ti matrix. The ultimate compressive strength ranged from 1019 MPa to 767 MPa for alloys with 21-25% porosities and from 173 MPa to 78 MPa for alloys with 50-56% porosities. Noted that adding a space holder agent played a more critical role in the mechanical behaviors of the alloys compared to adding niobium. The pores were largely open and exhibited irregular shapes, with uniform size distribution, allowing for cell ingrowth. Histological analysis showed that the alloys studied met the biocompatibility criteria required for orthopaedic biomaterial use.