Abstract
The effect of layer spacing and halogenation on the gas separation performances of free-standing smectic LC polymer membranes is being investigated by molecular engineering. LC membranes with various layer spacings and halogenated LCs were fabricated while having a planar aligned smectic morphology. Single permeation and sorption data show a correlation between gas diffusion and layer spacing, which results in increasing gas permeabilities with increasing layer spacing while the ideal gas selectivity of He over CO2 or He over N2 decreases. The calculated diffusion coefficients show a 6-fold increase when going from membranes with a layer spacing of 31.9 Å to membranes with a layer spacing of 45.2 Å, demonstrating that the layer spacing in smectic LC membranes mainly affects the diffusion of gasses rather than their solubility. A comparison of gas sorption and permeation performances of smectic LC membranes with and without halogenated LCs shows only a limited effect of LC halogenation by a slight increase in both solubility and diffusion coefficients for the membranes with halogenated LCs, resulting in a slightly higher gas permeation and increased ideal gas selectivities towards CO2. These results show that layer spacing plays an important role in the gas separation performances of smectic LC polymer membranes.